ABSTRACT
Objective: The purpose of this study was to evaluate the effects of blood contamination and haemostatic agents such as Ankaferd Blood Stopper (ABS) and hydrogen peroxide (H2O2) on the microtensile bond strength between dual cured resin cement-dentin interface. Material and Methods: Twelve pressed lithium disilicate glass ceramics were luted to flat occlusal dentin surfaces with Panavia F under the following conditions: Control Group: no contamination, Group Blood: blood contamination, Group ABS: ABS contamination Group H2O2: H2O2 contamination. The specimens were sectioned to the beams and microtensile testing was carried out. Failure modes were classified under stereomicroscope. Two specimens were randomly selected from each group, and SEM analyses were performed. Results: There were significant differences in microtensile bond strengths (µTBS) between the control and blood-contaminated groups (p<0.05), whereas there were no significant differences found between the control and the other groups (p>0.05). Conclusions: Contamination by blood of dentin surface prior to bonding reduced the bond strength between resin cement and the dentin. Ankaferd Blood Stoper and H2O2 could be used safely as blood stopping agents during cementation of all-ceramics to dentin to prevent bond failure due to blood contamination.
Subject(s)
Humans , Blood , Dental Bonding/methods , Dentin/chemistry , Hemostatics/chemistry , Resin Cements/chemistry , Dental Restoration Failure , Equipment Contamination , Hydrogen Peroxide/chemistry , Materials Testing , Microscopy, Electron, Scanning , Plant Extracts/chemistry , Shear Strength , Statistics as Topic , Surface Properties , Tensile StrengthABSTRACT
OBJECTIVES: This study investigated the possible interactions between three addition silicone materials (Express®, Aquasil Ultra® and Adsil®), three hemostatic agents (ferric sulfate, StatGel FS®; aluminum sulfate, GelCord®; and aluminum chloride, Hemostop®) and gingival retraction cords previously handled with latex gloves to determine whether direct contact with medicaments or indirect contamination by latex in conditions similar to those found in clinical practice inhibit or affect the setting of the impression materials. MATERIAL AND METHODS: A portable device for the simultaneous test of several specimens was specifically developed for this study. Polymerization inhibition was analyzed by examination of the impressions and the molded surface. Ten trials were performed for each addition silicone material used in the study, at a total of 240 study samples. RESULTS: All the samples tested (N=240) were nonreactive regardless of the type of combination used. CONCLUSIONS: Aluminum sulfate, ferric sulfate and aluminum chloride hemostatic solutions did not show any inhibitory potential on the addition silicone samples under study, and there were no changes in polymerization as a result of contact between addition silicone and retraction cords handled with latex gloves.
Subject(s)
Dental Impression Materials/chemistry , Gloves, Surgical , Hemostatics/chemistry , Latex/chemistry , Polymerization/drug effects , Polyvinyls/chemistry , Siloxanes/chemistry , Sulfur/chemistry , Gingival Retraction Techniques , Materials Testing , Surface Properties , Silicones/chemistryABSTRACT
Biosurgical preparations designed to promote surgical hemostasis and tissue adhesion are being increasingly employed across all surgical disciplines. Fibrin sealant is the most widely studied and utilized biosurgical adjunct in urology. Complex reconstructive, oncologic, and laparoscopic genitourinary procedures are those most appropriate for sealant use. This article details the diverse urologic applications of fibrin sealant in the management of genitourinary injuries, surgery, and complications.